Study on the Effect of Grain Refiner : On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications

Prasenjit Singha

ISBN 10: 6205499843 / ISBN 13: 9786205499849

Editore: LAP LAMBERT Academic Publishing, 2022

Riguardo questo articolo

nach der Bestellung gedruckt Neuware - Printed after ordering - Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold rolled to 55- 65% thickness reduction. The rolled material in the case of Alloy-2 is annealed at 490 for 4 hours and then subsequently aged for various intervals of times, whereas Alloy 1 is annealed at 5400C for 4 hours. The annealing temperatures are selected based on DSC analysis. Detailed microstructural and precipitations characterizations have been carried out for cast, rolled, and aged samples by Optical Microscopy, SEM, XRD, and EBSD analysis. The precipitates of Mg2Si and Si3Mg2 are observed in both Alloy-1 and Alloy-2, whereas TiB2 is observed in only Alloy-2 due to the presence of Ti and B as a grain refiners. This type of precipitates is observed at peak aged conditions. The mechanical properties like bulk hardness, nano-hardness, and room temperature tensile properties have been studied for both alloys. In case alloy 2, due to the grain refinement effect, the average grain size of the cast sample is reduced from (55.283±1.91) µm to (42.886±1.20) µm.

Codice articolo 9786205499849

Dati bibliografici

• Titolo: Study on the Effect of Grain Refiner : On Microstructure and Mechanical Properties of 6000XAluminum Alloys in Automobile Applications
• Editore: LAP LAMBERT Academic Publishing
• Data di pubblicazione: 2022
• Lingua: Inglese
• ISBN 10: 6205499843
• ISBN 13: 9786205499849
• Rilegatura: Taschenbuch
• Condizione: Neu
• Dimensioni: 220 L x 150 A x 4 P (millimetri) 220 millimetri di larghezza per 150 millimetri di altezza per 4 millimetri di profondità
• Peso: 96 grammi

Descrizione articolo

Riassunto

Two different types of alloys, namely alloy- 1 and Alloy-2, have been designed and produced using a melting casting route. Homogenized alloys are further cold rolled to 55- 65% thickness reduction. The rolled material in the case of Alloy-2 is annealed at 490℃ for 4 hours and then subsequently aged for various intervals of times, whereas Alloy 1 is annealed at 5400C for 4 hours. The annealing temperatures are selected based on DSC analysis. Detailed microstructural and precipitations characterizations have been carried out for cast, rolled, and aged samples by Optical Microscopy, SEM, XRD, and EBSD analysis. The precipitates of Mg2Si and Si3Mg2 are observed in both Alloy-1 and Alloy-2, whereas TiB2 is observed in only Alloy-2 due to the presence of Ti and B as a grain refiners. This type of precipitates is observed at peak aged conditions. The mechanical properties like bulk hardness, nano-hardness, and room temperature tensile properties have been studied for both alloys. In case alloy 2, due to the grain refinement effect, the average grain size of the cast sample is reduced from (55.283±1.91) µm to (42.886±1.20) µm.