9783330805972 - Extract Neem Tree as Corrosion Inhibitor di Abdel-Rahman, Ibrahim (6 risultati)

Paperback. Condizione: Brand New. 52 pages. 8.66x5.91x0.12 inches. In Stock.

Taschenbuch. Condizione: Neu. Extract Neem Tree as Corrosion Inhibitor | Ibrahim Abdel-Rahman | Taschenbuch | 52 S. | Englisch | 2017 | Noor Publishing | EAN 9783330805972 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu.

Taschenbuch. Condizione: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -The effect of aqueous extract of UAE Neem (Azadirachta Indica) on the corrosion inhibition of carbon steel in 1.0MHCl solution was investigated electrochemically, and by weight-loss experiments at temperatures ranging from 303 to 343 K. The percentage inhibition increased with the increase of the concentration of the inhibitor. At a concentration of 2.0 g/L, the percentage inhibition reached about 87% at room temperature and 80% at 303 K. The percentage inhibition decreased with the increase of temperature. The thermodynamic parameters for the adsorption of this inhibitor on the metal surface were calculated using the Temkin adsorption isotherm. The aqueous Neem leaves extract was found to be an excellent potential corrosion inhibitor because of the high content of tannin content as well as the presence of a series of complex triterpene glycosides. 52 pp. Englisch.

Condizione: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Abdel-Rahman IbrahimBiographyIbrahim Abdel-Rahman was born in Bedya, Palestine in 1958. He is a lecturer at University of Sharjah since 2000. He was a lecturer at the Applied Science University (Jordan) (1994-2000). He was the head o.

Taschenbuch. Condizione: Neu. This item is printed on demand - Print on Demand Titel. Neuware -The effect of aqueous extract of UAE Neem (Azadirachta Indica) on the corrosion inhibition of carbon steel in 1.0MHCl solution was investigated electrochemically, and by weight-loss experiments at temperatures ranging from 303 to 343 K. The percentage inhibition increased with the increase of the concentration of the inhibitor. At a concentration of 2.0 g/L, the percentage inhibition reached about 87% at room temperature and 80% at 303 K. The percentage inhibition decreased with the increase of temperature. The thermodynamic parameters for the adsorption of this inhibitor on the metal surface were calculated using the Temkin adsorption isotherm. The aqueous Neem leaves extract was found to be an excellent potential corrosion inhibitor because of the high content of tannin content as well as the presence of a series of complex triterpene glycosides.Books on Demand GmbH, Überseering 33, 22297 Hamburg 52 pp. Englisch.

Taschenbuch. Condizione: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - The effect of aqueous extract of UAE Neem (Azadirachta Indica) on the corrosion inhibition of carbon steel in 1.0MHCl solution was investigated electrochemically, and by weight-loss experiments at temperatures ranging from 303 to 343 K. The percentage inhibition increased with the increase of the concentration of the inhibitor. At a concentration of 2.0 g/L, the percentage inhibition reached about 87% at room temperature and 80% at 303 K. The percentage inhibition decreased with the increase of temperature. The thermodynamic parameters for the adsorption of this inhibitor on the metal surface were calculated using the Temkin adsorption isotherm. The aqueous Neem leaves extract was found to be an excellent potential corrosion inhibitor because of the high content of tannin content as well as the presence of a series of complex triterpene glycosides.