Isbn: 9783659618826 - controlled low-strength material using thermal power plant ash (6 risultati)

Taschenbuch. Condizione: Neu. Controlled low-strength material using thermal power plant ash | Sivakumar Naganathan (u. a.) | Taschenbuch | 132 S. | Englisch | 2014 | LAP LAMBERT Academic Publishing | EAN 9783659618826 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu. …

paperback. Condizione: New. NEW. SHIPS FROM MULTIPLE LOCATIONS. book.

Taschenbuch. Condizione: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -Controlled low strength material (CLSM) is self-compacting flowable fill which is primarily used as backfill. This book presents the investigation done on CLSM mixtures made using NaOH, lime, bottom ash, fly ash, and water. A series of experiments on fresh state, viz. flowability, fresh density, segregation resistance and bleeding were conducted. The CLSM mixtures were also tested for water absorption, hardened density, ultrasonic pulse velocity and compressive strength at hardened state. The flowability of all samples is 300 ± 20 mm and increase in FA/binder ratio reduces the flowability of mixture. All the CLSM mixtures were classified as normal weight. All samples had good segregation resistance with non-corrosive behavior. Durability properties of CLSM were satisfactory. Compressive strength of mixtures varied between 1.1 MPa to 3.35 MPa. Increment of lime and NaOH leads to increment in strength only at certain ratios. It is concluded that the CLSM mixtures produced in the investigation are cement-free, has good mechanical and durability properties and can be used in practical applications. 132 pp. Englisch.…

Taschenbuch. Condizione: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Controlled low strength material (CLSM) is self-compacting flowable fill which is primarily used as backfill. This book presents the investigation done on CLSM mixtures made using NaOH, lime, bottom ash, fly ash, and water. A series of experiments on fresh state, viz. flowability, fresh density, segregation resistance and bleeding were conducted. The CLSM mixtures were also tested for water absorption, hardened density, ultrasonic pulse velocity and compressive strength at hardened state. The flowability of all samples is 300 ± 20 mm and increase in FA/binder ratio reduces the flowability of mixture. All the CLSM mixtures were classified as normal weight. All samples had good segregation resistance with non-corrosive behavior. Durability properties of CLSM were satisfactory. Compressive strength of mixtures varied between 1.1 MPa to 3.35 MPa. Increment of lime and NaOH leads to increment in strength only at certain ratios. It is concluded that the CLSM mixtures produced in the investigation are cement-free, has good mechanical and durability properties and can be used in practical applications. …

Condizione: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Naganathan SivakumarDr. Sivakumar Naganathan is working as an Associate Professor in the department of civil engineering, Universiti Tenaga Nasional (UNITEN), Malaysia. Mr. Shojaeddin Jamali is an alumni of UNITEN, currently working . …

Taschenbuch. Condizione: Neu. This item is printed on demand - Print on Demand Titel. Neuware -Controlled low strength material (CLSM) is self-compacting flowable fill which is primarily used as backfill. This book presents the investigation done on CLSM mixtures made using NaOH, lime, bottom ash, fly ash, and water. A series of experiments on fresh state, viz. flowability, fresh density, segregation resistance and bleeding were conducted. The CLSM mixtures were also tested for water absorption, hardened density, ultrasonic pulse velocity and compressive strength at hardened state. The flowability of all samples is 300 ± 20 mm and increase in FA/binder ratio reduces the flowability of mixture. All the CLSM mixtures were classified as normal weight. All samples had good segregation resistance with non-corrosive behavior. Durability properties of CLSM were satisfactory. Compressive strength of mixtures varied between 1.1 MPa to 3.35 MPa. Increment of lime and NaOH leads to increment in strength only at certain ratios. It is concluded that the CLSM mixtures produced in the investigation are cement-free, has good mechanical and durability properties and can be used in practical applications.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 132 pp. Englisch. …