ISBN: 9786202516358 - characterization of fly ash-cold setting resin powder: fly ash-cold setting resin powder (5 risultati)

Taschenbuch. Condizione: Neu. Characterization of Fly Ash-Cold Setting Resin Powder | Fly Ash-Cold Setting Resin Powder | Satyajeet Kumar (u. a.) | Taschenbuch | 56 S. | Englisch | 2020 | LAP LAMBERT Academic Publishing | EAN 9786202516358 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu. …

Taschenbuch. Condizione: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -Industrial waste like fly-ash which is creating environmental problems is mainly used as a building material due to its low cost and easy availability. The main disadvantage of these bricks is its low strength. So, a lot of research is going on to increase the strength of these bricks. The present research work is carried out to develop a new systematic procedure to produce fly ash composite bricks which will have higher compressive strength. Here the fly-ash is mixed with Cold setting resin at different proportions and water treated at different temperatures to find out a solution to the brick industry. The compressive strength, Hardness, water absorption, density and thermal conductivity of the fly ash-resin powder bricks obtained under optimum test conditions are 11.24 MPa, 47.37HV, 19.09% 1.68 g/cm3, and 0.055 W/mK respectively. The sliding wear behavior is also investigated. The structure-property correlation of these composites is studied using X-ray diffraction, FTIR analysis, and scanning electron microscopy. 56 pp. Englisch.…

Taschenbuch. Condizione: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Industrial waste like fly-ash which is creating environmental problems is mainly used as a building material due to its low cost and easy availability. The main disadvantage of these bricks is its low strength. So, a lot of research is going on to increase the strength of these bricks. The present research work is carried out to develop a new systematic procedure to produce fly ash composite bricks which will have higher compressive strength. Here the fly-ash is mixed with Cold setting resin at different proportions and water treated at different temperatures to find out a solution to the brick industry. The compressive strength, Hardness, water absorption, density and thermal conductivity of the fly ash-resin powder bricks obtained under optimum test conditions are 11.24 MPa, 47.37HV, 19.09% 1.68 g/cm3, and 0.055 W/mK respectively. The sliding wear behavior is also investigated. The structure-property correlation of these composites is studied using X-ray diffraction, FTIR analysis, and scanning electron microscopy.…

Condizione: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: Kumar SatyajeetMr. Satyajeet Kumar and Dr. Ashutosh Pattanaik have completed their M.Tech and Ph.D. respectively in Metallurgical & Materials Engineering from the National Institute Of Technology, Rourkela. Mr. Kumar is currently wor.…

Taschenbuch. Condizione: Neu. This item is printed on demand - Print on Demand Titel. Neuware -Industrial waste like fly-ash which is creating environmental problems is mainly used as a building material due to its low cost and easy availability. The main disadvantage of these bricks is its low strength. So, a lot of research is going on to increase the strength of these bricks. The present research work is carried out to develop a new systematic procedure to produce fly ash composite bricks which will have higher compressive strength. Here the fly-ash is mixed with Cold setting resin at different proportions and water treated at different temperatures to find out a solution to the brick industry. The compressive strength, Hardness, water absorption, density and thermal conductivity of the fly ash-resin powder bricks obtained under optimum test conditions are 11.24 MPa, 47.37HV, 19.09% 1.68 g/cm3, and 0.055 W/mK respectively. The sliding wear behavior is also investigated. The structure-property correlation of these composites is studied using X-ray diffraction, FTIR analysis, and scanning electron microscopy.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 56 pp. Englisch.…