Articoli correlati a Fatigue Damage, Crack Growth and Life Prediction
Sinossi
Fatigue failure is a multi-stage process. It begins with the initiation of cracks, and with continued cyclic loading the cracks propagate, finally leading to the rupture of a component or specimen. The demarcation between the above stages is not well-defined. Depending upon the scale of interest, the variation may span three orders of magnitude. For example, to a material scientist an initiated crack may be of the order of a micron, whereas for an engineer it can be of the order of a millimetre. It is not surprising therefore to see that investigation of the fatigue process has followed different paths depending upon the scale of phenomenon under investigation. Interest in the study of fatigue failure increased with the advent of industrial ization. Because of the urgent need to design against fatigue failure, early investiga tors focused on prototype testing and proposed failure criteria similar to design formulae. Thus, a methodology developed whereby the fatigue theories were proposed based on experimental observations, albeit at times with limited scope. This type of phenomenological approach progressed rapidly during the past four decades as closed-loop testing machines became available.
Le informazioni nella sezione "Riassunto" possono far riferimento a edizioni diverse di questo titolo.
Contenuti
Some general concepts concerning fatigue. Cyclic stress-strain response. Phenomenological approach to fatigue life prediction under uniaxial loading. Fatigue failure under multiaxial states of stress. Multiaxial experimental facilities. Constitutive laws for transient and stable behaviour of inelastic solids. Fatigue crack growth. Fatigue of notched members. Growth and behaviour of small cracks. Probabilistic fatigue crack growth. References. Index.
Le informazioni nella sezione "Su questo libro" possono far riferimento a edizioni diverse di questo titolo.
Compra nuovo
Visualizza questo articolo
EUR 180,07
EUR 9,70 per la spedizione da Germania a Italia
Destinazione, tempi e costi
Risultati della ricerca per Fatigue Damage, Crack Growth and Life Prediction
Immagini fornite dal venditore
Fatigue Damage, Crack Growth and Life Prediction
Print on DemandDa: moluna, Greven, Germania
Valutazione del venditore 5 su 5 stelle
Condizione: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Fatigue failure is a multi-stage process. It begins with the initiation of cracks, and with continued cyclic loading the cracks propagate, finally leading to the rupture of a component or specimen. The demarcation between the above stages is not well-define. Codice articolo 5833779
Quantità: Più di 20 disponibili
Foto dell'editore
Fatigue Damage, Crack Growth and Life Prediction
Da: Best Price, Torrance, CA, U.S.A.
Valutazione del venditore 5 su 5 stelle
Condizione: New. SUPER FAST SHIPPING. Codice articolo 9789401071758
Quantità: 2 disponibili
Immagini fornite dal venditore
Fatigue Damage, Crack Growth and Life Prediction
Editore:
Springer Netherlands, Springer Netherlands Sep 2011, 2011
ISBN 10: 9401071756
ISBN 13: 9789401071758
Nuovo
Taschenbuch
Da: buchversandmimpf2000, Emtmannsberg, BAYE, Germania
Valutazione del venditore 5 su 5 stelle
Taschenbuch. Condizione: Neu. This item is printed on demand - Print on Demand Titel. Neuware -Fatigue failure is a multi-stage process. It begins with the initiation of cracks, and with continued cyclic loading the cracks propagate, finally leading to the rupture of a component or specimen. The demarcation between the above stages is not well-defined. Depending upon the scale of interest, the variation may span three orders of magnitude. For example, to a material scientist an initiated crack may be of the order of a micron, whereas for an engineer it can be of the order of a millimetre. It is not surprising therefore to see that investigation of the fatigue process has followed different paths depending upon the scale of phenomenon under investigation. Interest in the study of fatigue failure increased with the advent of industrial ization. Because of the urgent need to design against fatigue failure, early investiga tors focused on prototype testing and proposed failure criteria similar to design formulae. Thus, a methodology developed whereby the fatigue theories were proposed based on experimental observations, albeit at times with limited scope. This type of phenomenological approach progressed rapidly during the past four decades as closed-loop testing machines became available.Springer Verlag GmbH, Tiergartenstr. 17, 69121 Heidelberg 488 pp. Englisch. Codice articolo 9789401071758
Quantità: 1 disponibili
Foto dell'editore
Fatigue Damage, Crack Growth and Life Prediction
Da: Ria Christie Collections, Uxbridge, Regno Unito
Valutazione del venditore 5 su 5 stelle
Condizione: New. In. Codice articolo ria9789401071758_new
Quantità: Più di 20 disponibili
Immagini fornite dal venditore
Fatigue Damage, Crack Growth and Life Prediction
Da: AHA-BUCH GmbH, Einbeck, Germania
Valutazione del venditore 5 su 5 stelle
Taschenbuch. Condizione: Neu. Druck auf Anfrage Neuware - Printed after ordering - Fatigue failure is a multi-stage process. It begins with the initiation of cracks, and with continued cyclic loading the cracks propagate, finally leading to the rupture of a component or specimen. The demarcation between the above stages is not well-defined. Depending upon the scale of interest, the variation may span three orders of magnitude. For example, to a material scientist an initiated crack may be of the order of a micron, whereas for an engineer it can be of the order of a millimetre. It is not surprising therefore to see that investigation of the fatigue process has followed different paths depending upon the scale of phenomenon under investigation. Interest in the study of fatigue failure increased with the advent of industrial ization. Because of the urgent need to design against fatigue failure, early investiga tors focused on prototype testing and proposed failure criteria similar to design formulae. Thus, a methodology developed whereby the fatigue theories were proposed based on experimental observations, albeit at times with limited scope. This type of phenomenological approach progressed rapidly during the past four decades as closed-loop testing machines became available. Codice articolo 9789401071758
Quantità: 1 disponibili
Foto dell'editore
Fatigue Damage, Crack Growth and Life Prediction
Da: Lucky's Textbooks, Dallas, TX, U.S.A.
Valutazione del venditore 5 su 5 stelle
Condizione: New. Codice articolo ABLIING23Apr0412070056867
Quantità: Più di 20 disponibili
Foto dell'editore
Fatigue Damage, Crack Growth and Life Prediction
Da: Books Puddle, New York, NY, U.S.A.
Valutazione del venditore 4 su 5 stelle
Condizione: New. pp. 488 Index. Codice articolo 2654517983
Quantità: 4 disponibili
Foto dell'editore
Fatigue Damage, Crack Growth and Life Prediction
Print on DemandDa: Majestic Books, Hounslow, Regno Unito
Valutazione del venditore 5 su 5 stelle
Condizione: New. Print on Demand pp. 488 49:B&W 6.14 x 9.21 in or 234 x 156 mm (Royal 8vo) Perfect Bound on White w/Gloss Lam. Codice articolo 55074560
Quantità: 4 disponibili
Foto dell'editore
Fatigue Damage, Crack Growth and Life Prediction
Print on DemandDa: Biblios, Frankfurt am main, HESSE, Germania
Valutazione del venditore 5 su 5 stelle
Condizione: New. PRINT ON DEMAND pp. 488. Codice articolo 1854517973
Quantità: 4 disponibili
Immagini fornite dal venditore
Fatigue Damage, Crack Growth and Life Prediction
Editore:
Springer Netherlands Sep 2011, 2011
ISBN 10: 9401071756
ISBN 13: 9789401071758
Nuovo
Taschenbuch
Da: BuchWeltWeit Ludwig Meier e.K., Bergisch Gladbach, Germania
Valutazione del venditore 5 su 5 stelle
Taschenbuch. Condizione: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -Fatigue failure is a multi-stage process. It begins with the initiation of cracks, and with continued cyclic loading the cracks propagate, finally leading to the rupture of a component or specimen. The demarcation between the above stages is not well-defined. Depending upon the scale of interest, the variation may span three orders of magnitude. For example, to a material scientist an initiated crack may be of the order of a micron, whereas for an engineer it can be of the order of a millimetre. It is not surprising therefore to see that investigation of the fatigue process has followed different paths depending upon the scale of phenomenon under investigation. Interest in the study of fatigue failure increased with the advent of industrial ization. Because of the urgent need to design against fatigue failure, early investiga tors focused on prototype testing and proposed failure criteria similar to design formulae. Thus, a methodology developed whereby the fatigue theories were proposed based on experimental observations, albeit at times with limited scope. This type of phenomenological approach progressed rapidly during the past four decades as closed-loop testing machines became available. 488 pp. Englisch. Codice articolo 9789401071758
Quantità: 2 disponibili