dalya k naser (9 risultati)

Condizione: New.

Paperback. Condizione: Brand New. 180 pages. 8.66x5.91x0.41 inches. In Stock.

Taschenbuch. Condizione: Neu. The Effect of Magnetic & Electric Fields on Surface Plasmon Resonance | Nano and Plasma | Dalya K. Naser (u. a.) | Taschenbuch | 180 S. | Englisch | 2017 | LAP LAMBERT Academic Publishing | EAN 9783330056268 | Verantwortliche Person für die EU: preigu GmbH & Co. KG, Lengericher Landstr. 19, 49078 Osnabrück, mail[at]preigu[dot]de | Anbieter: preigu.

Taschenbuch. Condizione: Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -Nanoparticles are prepared by using Q-switching Nd:YAG laser (1064) nm of (Pt, Au, Ag, Cu) targets immersed in different solvent (distillwater DW, deionized water DI, distillwater with additive 0.15mM of poly(N-vinylpyrrolidone (C6H9NO)x (PVP)) with different laser power (100,300,500)mJ/pulse, 300 pulse, and the distance between laser and target is 15cm. Then prepared noble metals nanoparticles with electric field and with magnetic field in DW. The experimental parameters are the effect of the solvent, laser power (mJ/pulse), effect the electric and magnetic field on noble metals nanoparticles. The behavior of UV-VIS. Absorbance spectra associated with noble metals NPs (Pt, Au, Ag, Cu) were studied as a function of laser power shows when increased laser power increase peak intensity and shifts to smaller wavelength (blue shift). 180 pp. Englisch.

Condizione: New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Autor/Autorin: K. Naser DalyaDalya Khalid, Master General Physics Science, University of Wasit 2016, Bachelor of Science Physics University of Wasit, 2014.Nanoparticles are prepared by using Q-switching Nd:YAG laser (1064) nm of (Pt, Au, Ag, Cu.

Condizione: New. Print on Demand.

Condizione: New. PRINT ON DEMAND.

Taschenbuch. Condizione: Neu. This item is printed on demand - Print on Demand Titel. Neuware -Nanoparticles are prepared by using Q-switching Nd:YAG laser (1064) nm of (Pt, Au, Ag, Cu) targets immersed in different solvent (distillwater DW, deionized water DI, distillwater with additive 0.15mM of poly(N-vinylpyrrolidone (C6H9NO)x (PVP)) with different laser power (100,300,500)mJ/pulse, 300 pulse, and the distance between laser and target is 15cm. Then prepared noble metals nanoparticles with electric field and with magnetic field in DW. The experimental parameters are the effect of the solvent, laser power (mJ/pulse), effect the electric and magnetic field on noble metals nanoparticles. The behavior of UV-VIS. Absorbance spectra associated with noble metals NPs (Pt, Au, Ag, Cu) were studied as a function of laser power shows when increased laser power increase peak intensity and shifts to smaller wavelength (blue shift).VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 180 pp. Englisch.

Taschenbuch. Condizione: Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Nanoparticles are prepared by using Q-switching Nd:YAG laser (1064) nm of (Pt, Au, Ag, Cu) targets immersed in different solvent (distillwater DW, deionized water DI, distillwater with additive 0.15mM of poly(N-vinylpyrrolidone (C6H9NO)x (PVP)) with different laser power (100,300,500)mJ/pulse, 300 pulse, and the distance between laser and target is 15cm. Then prepared noble metals nanoparticles with electric field and with magnetic field in DW. The experimental parameters are the effect of the solvent, laser power (mJ/pulse), effect the electric and magnetic field on noble metals nanoparticles. The behavior of UV-VIS. Absorbance spectra associated with noble metals NPs (Pt, Au, Ag, Cu) were studied as a function of laser power shows when increased laser power increase peak intensity and shifts to smaller wavelength (blue shift).